dc.description.abstract	El zirconio es una cerámica policristalina utilizada para restauraciones libres de metal. Esta no posee matriz vítrea, por tanto, los procedimientos de cementación con previo acondicionamiento ácido no son efectivos. Actualmente, se cuentan con distintos tipos de agentes cementantes para estas restauraciones con imprimadores ricos en 10 MDP que junto con el uso de la microabrasión de las superficies permiten una retención mecánica y una unión físico-química estable en el tiempo. Recientemente, se han propuesto nuevos cementos basados en vidrios bioactivos, los cuales presentan como beneficio adicional, el cierre de brechas marginales a través de la remineralización de la dentina. Sin embargo, existen pocos estudios que evalúen su resistencia adhesiva y la comparen con los sistemas de cementación ricos en MDP. Por tanto, el objetivo de este estudio fue evaluar la fuerza adhesiva al zirconio de 2 cementos bioactivos: "Ceramir®" y Theracem®. En este estudio experimental in vitro se usó una muestra probabilística de 30 muestras por cada uno de los tres grupos evaluado: los dos cementos biactivos y un cemento control Relyx™ Ultimate. Cada unidad muestral consistió en un cilindro de 1mm H X 0.5mm de diámetro cementado a láminas maquinadas de zirconio translucido de 1.5mm[h] X 1.2mm[L] X 5mm [W] arenadas con óxido de aluminio de 50 micras. Para la fabricación de cada cilindro se utilizó como molde un tubo de Tygon® Las muestras serán sometidas a proceso de termociclado (5000 ciclos de 1 minuto cada uno a temperaturas de 5 a 55°) y posteriormente a la prueba de resistencia adhesiva en la máquina universal de pruebas. Los datos serán expresados en MPa serán analizados descriptivamente mediante medidas de tendencia central y de dispersión. Para determinar si los datos siguen una distribución normal se utilizará la prueba Shapiro-Wilk,dependiendo de la normalidad de los datos se usará la prueba de ANOVA a una vía o de Kruskar-Wallis. En resultados parciales encontró que el 23.33 % del grupo Ceramir se perdió durante el fraguado del cemento y 76.66% durante el retiro del tygon. En los grupos Theracem y Relyx Ultimate no se observaron perdidas de muestras durante la fabricación.	spa
dc.description.abstractenglish	Zirconium is a polycrystalline ceramic used for metal-free restorations because it has no vitreous matrix, so cementation procedures with previous acid conditioning are not effective. There are different agents for said restorations rich in 10MDP primers, which along with micro-abrasion of the surfaces allow a stable mechanical retention and physical-chemical union. New cements based on bio-active glass have been proposed which present the filling of marginal gaps by re-mineralising the dentin. However, there are few studies which evaluate its adhesive strength and compare it with systems rich in MDP so the aim of this study was to do so with two bio-active cements: Ceramir®" y Theracem® on Zirconium. A probabilistic trial of 30 samples for each of the three evaluation groups was used: two bio-active cements and the control Relyx™ Ultimate. Each consisted of a 1 mm cylinder H X 0.5 mm cemented to transparent 1.5mm[h] X 1.2mm[L] X 5mm [W] zirconium machined plates sanded with 50 micron aluminium oxide. A tube of Tygon® was used for the fabrication of the cylinders and the samples will be subject to a thermocycled process (5000 one-minute cycles at temperatures between 5 ˚ and 55 ˚) after which the strength trial in the universal testing machine will be carried out. Results will be expressed in MPa and analysed descriptively with central tendency and dispersion measurements. The Shapiro-Wilk test will be used to determine if data follows a normal distribution and one-way ANOVA or Kruskar-Wallis tests depending on the normality of data. Partial results showed that 23.33% of the Ceramir group was lost during setting and 76.66% during the Tygon removal. No losses were reported during fabrication with the Theracem and Relyx Ultimate groups.	eng
dc.description.degreelevel	Especialización	spa
dc.description.degreename	Especialista en prostodoncia	spa
dc.format.mimetype	application/pdf
dc.identifier.instname	instname:Universidad El Bosque	spa
dc.identifier.reponame	reponame:Repositorio Institucional Universidad El Bosque	spa
dc.identifier.repourl	repourl:https://repositorio.unbosque.edu.co
dc.identifier.uri	https://hdl.handle.net/20.500.12495/8380
dc.language.iso	spa
dc.publisher.faculty	Facultad de Odontología	spa
dc.publisher.grantor	Universidad El Bosque	spa
dc.publisher.program	Especialización en prostodoncia	spa
dc.rights	Attribution-NonCommercial-ShareAlike 4.0 International	*
dc.rights.accessrights	https://purl.org/coar/access_right/c_abf2
dc.rights.accessrights	info:eu-repo/semantics/openAccess
dc.rights.creativecommons	2020-08
dc.rights.local	Acceso abierto	spa
dc.rights.uri	https://creativecommons.org/licenses/by-nc-sa/4.0/	*
dc.subject	Fuerza adhesiva	spa
dc.subject	Cementos de resina	spa
dc.subject	Cementos bioceramicos	spa
dc.subject	Agentes cementantes	spa
dc.subject	Cementos resinosos	spa
dc.subject	Zirconio	spa
dc.subject.keywords	Resin cements	spa
dc.subject.keywords	Bio-ceramic cements	spa
dc.subject.keywords	Cementing agents	spa
dc.subject.keywords	Resinous cements	spa
dc.subject.keywords	Zirconium	spa
dc.subject.keywords	Adhesive strength	spa
dc.subject.nlm	WU 500
dc.title	Evaluación de la fuerza adhesiva al zirconio de 2 cementos bioactivos: "Ceramir®" y Theracem ®. Resultados preliminares	spa
dc.title.translated	Evaluation of the adhesive strength on zirconium of two bio-active cements: Ceramir® and Theracem®. Preliminary results	spa
dc.type.coar	https://purl.org/coar/resource_type/c_7a1f
dc.type.coarversion	https://purl.org/coar/version/c_970fb48d4fbd8a85
dc.type.driver	info:eu-repo/semantics/bachelorThesis
dc.type.hasversion	info:eu-repo/semantics/acceptedVersion
dc.type.local	Tesis/Trabajo de grado - Monografía - Especialización	spa

Evaluación de la fuerza adhesiva al zirconio de 2 cementos bioactivos: "Ceramir®" y Theracem ®. Resultados preliminares

Archivos

Bloque original

Bloque de licencias

Colecciones